| 專利摘要 | 本發明係有關於一種水溶性砂模及其製造方法，其係提供一水溶性砂模用於作為複合材料製程之一次性模具，其中水溶性砂模包含一聚乙烯醇溶劑與一二氧化矽矽砂，且聚乙烯醇溶劑包含聚乙烯醇、酒精與水。一開始先提供聚乙烯醇溶劑攪拌二氧化矽矽砂，而混合形成一砂模材料；接著，傾倒砂模材料至一模具之一模穴中；隨後加熱烘烤包含砂模材料之模具，以使模穴中之砂模材料硬化成型為一砂模；接續於移除固定砂模之模具後，修整砂模之表面，以完成砂模之製備而用於複合材料製程。複合材料製程完成後即利用水溶解聚乙烯醇溶劑而瓦解砂模，進而取得複合材料製成之成品。 The present invention relates to a water-soluble sand-cast and the method for manufacturing thereof, which provides the water-soluble sand-cast to be a disposable cast of composite products process. The sand-cast includes a solvent of Polyvinyl alcohol and a sand. First the solvent of Polyvinyl alcohol is provided to mix the sand for getting an material of sand-cast. The material of the sand-cast is therefore dumped into a modeling hole of a cast. The cast having the material of the sand-cast is warmed up and baked to form and harden the sand-cast. The sand-cast is further baked until the case of the sand cast is completely hardened after removing the cast fixed sand-cast. After finishing the composite manufacturing process, the solvent of Polyvinyl alcohol is dissolved with water to crash the sand-cast for getting the end item of composite products. 【創作特點】 本發明之主要目的，在於提供一種水溶性砂模及其製造方法，其係提供一聚乙烯醇溶劑結合一二氧化矽矽砂作為一砂模原料，並將砂模原料倒入一模具之一模穴中，即可藉由加熱烘烤成型，進而應用於量產砂模。本發明之次要目的，在於提供一種水溶性砂模及其製造方法，其係塗佈顏料至該砂模之表面，並包覆離型膜材料至砂模之表面，以讓該砂模於後續加工作業完成後可順利脫膜而取出成品。本發明為一種水溶性砂模及其製造方法，其係提供包含一聚乙烯醇溶劑與一二氧化矽矽砂之一砂模，以運用於鑄造用途上。製造本發明之砂模時，其執行之步驟係先提供該聚乙烯醇溶劑混合該二氧化矽矽砂，以取得一砂模材料，其中該聚乙烯醇溶劑係包含聚乙烯醇、酒精與水；接續，將所得之該砂模材料倒入一模具之一模穴之中；然後，加熱烘烤容置該砂模材料之該模具至該砂模半硬化後，移除該模具，以使半硬化之該砂模加熱至完全硬化成型；最後修整該砂模之表面，以使該砂模之表面更加光滑。另外，本發明之砂模更利用塗佈顏料至該砂模之表面，以及使用一離型膜材料包覆該砂模之表面，以使該砂模完成後續之加工作業。 |