| 專利摘要 | In this patent, a high energy and power density supercapacitor was invented. A coin cell with supercapacitor includes a spring lamination, a working electrode, a counter electrode, a separator, and an Organic electrolyte. The working and counter electrodes were Activated carbon/N-doping porous graphene/binder coated on Aluminum substrate. The separator was from Nippon Kodoshi Corporation. The Organic electrolyte was 1M TEABF4/PC. The method of producing N-doping porous graphene included the following steps: Step 1: Graphite oxide (GO) was transferred into the furnace. Step 2: Inject 50 c.c./min gas flow of Nitrous oxides for one hour. Step 3: Intensify 40 Celsius degrees/min to 900 Celsius degrees and after holding for one hour, lower the temperature naturally to the room temperature, it can be prepared into N-doping porous graphene. In this patent, the capacitance of the supercapacitor is 122 F/g and the power density is 31 kW/Kg. |